Ateva® 1615
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H8gxBK_Ateva-1615.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is well suited for extrusion coating, coextrusion and specialty lamination applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 16.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 33 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 12.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 720 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 90.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT PCR PA66 G33-300PCR | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT PCR |
| NILENE® P3 K20VA | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| NuSil CV-9042 | NuSil Technology | Silicone | NuSil |
| LNP™ LUBRICOMP™ WCL36 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| MACOMASS TPE MM-TPE V 5020 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |