| Category: | PLA , Polylactic Acid |
| Manufacturer: | TER HELL PLASTIC GMBH |
| Trademark: | TEREZ NatureGran |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H8c2Ow_TEREZ-NatureGran-PO1000.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
|
Compound based on PLA. Partially based on renewable raw materials. Semitransparent. For injection moulding applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3570 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 51.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 62.0 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM 8 O TL | Arkema | Nylon 11 | Rilsan® |
| Baoding 67I90 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| ICORENE® N9903 | ICO Polymers EMEA, A Division of A. Schulman | Acrylic (PMMA) | ICORENE® |
| KARINTOX 70/2 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | KARINTOX |
| RTP 299 E X 141359 U | RTP Company | Nylon, Unspecified | RTP |