Order Products : sales@su-jiao.com
Ipethene® 100
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Ipethene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H8aWuf_Ipethene-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IPETHENE® 100 is a low density polyethylene extrusion grade, produced by high pressure autoclave technology. It exhibits very good mechanical strength, good processability and good bubble stability in thick blown film production. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 22.0 | MPa | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 650 | % | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 650 | % | ISO 527-3 |
| Dart Drop Impact 1(100 µm, Blown Film) | 470 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 100 µm, blown film | 0.031 | N | ISO 6383-2 |
| TD : 100 µm, blown film | 0.051 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306 |
| Melting Temperature 2 | 109 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Film properties: Measured on 100 µm blown film, Blow-up ratio 2.5:1, output 10 kg/h, melt temperature ~210 °C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | By DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9610 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| TiGlaze™ ST | Eastman Chemical Company | Copolyester | TiGlaze™ |
| Nypol® PA A3 G15 HS UV RH PRTA011 NR303 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Elastron® G G300.A55.B | Elastron USA, Inc. | SEBS | Elastron® G |
| POLYCASA® ACRYL G 66 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |