PENTAMID B E5 H natural
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7b1Ng_PENTAMIDBE5Hnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised and elastomeric modified polyamide 6 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.8 | -- | % | ISO 294-4 |
| Flow | 1.4 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 9.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2500 | 950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 65.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | 13 | % | ISO 527-2/50 |
| Flexural Modulus | 2600 | -- | MPa | ISO 178 |
| Flexural Stress | 90.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 100 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.2 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6-I, MHR, 14-030 N | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.18 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 275 | °C | |
| Middle Temperature | 260 - 285 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 55.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC HP5005A | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Stanyl® TW241F10 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Sylvin 9067F5 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WELLAMID Nylon 6600 MZ 401 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| INNOPOL® PP CS 1-3610 UW | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |