Wanthane® WHT-1570IC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7R6nR_WanthaneWHT1570IC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Extrusion and injection molding grade FEATURES: Free of platicizer, excellent abrasion and slip resistance, low temperature flexibility, good processability Applications: Electronic Parts, rigid / flexible composite systems, tools, shoes, compounds, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 50.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 3.50 | MPa | ASTM D412 |
| 300% strain | 6.50 | MPa | ASTM D412 |
| Tensile Strength (Break) | 30.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 700 | % | ASTM D412 |
| Tear Strength | 75.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 16 | % | ASTM D395 |
| 70°C, 22 hr | 48 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 65.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 195 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Adapter Temperature | 195 | °C | |
| Die Temperature | 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss SPVC8014 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Unspecified | Small Boss |
| UNISOFT TPE™ ST-46A-NT-2-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Elastane™ 4720-90A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Hanwha Total PP RP100N120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| 3M™ Dyneon™ PTFE Compound TF R4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |