Durethan® BG 30 X H3.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7LiAw_Durethan-BG-30-X-H3-0-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers/glass spheres, injection molding, heat-aging stabilized, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.80 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.30 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.50 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 185 | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 6210 | 3100 | MPa | ASTM D638 |
| 23°C | 6400 | 3100 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 121 | 62.7 | MPa | ASTM D638 |
| Break, 23°C | 120 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 4.0 | 10 | % | ASTM D638, ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 2400 | MPa | |
| 1000 hr | -- | 2000 | MPa | |
| Flexural Modulus | ||||
| 23°C | 5800 | 2800 | MPa | ASTM D790 |
| 23°C 5 | 5800 | 2800 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 195 | 100 | MPa | ASTM D790 |
| 3.5% Strain, 23°C | 170 | 80.0 | MPa | ISO 178/A |
| 23°C 6 | 185 | 100 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | 8.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6,GHR,14-060, (GB+GF)30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 45 | kJ/m² | |
| 23°C | 45 | 75 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 30 | 40 | kJ/m² | |
| 23°C | 35 | 60 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.70 | -- | J | |
| 23°C | 2.00 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 690 | -- | N | |
| 23°C | 700 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 9 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.50 | -- | ||
| 23°C, 1 MHz | 4.00 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.027 | -- | ||
| 23°C, 1 MHz | 0.022 | -- | ||
| Comparative Tracking Index (Solution A) | 375 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1204D | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Akulon® Ultraflow K-FHGR24 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Gallonprene® GP520-6004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LUCITE® 41 | Lucite International Inc. | Acrylic (PMMA) | LUCITE® |
| LTP ZE-2125 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |