LNP™ VERTON™ RVL36 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H5yhnE_LNP-VERTON-RVL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RVL36 is a compound based on Nylon 66 resin containing Long Glass Fiber, PTFE. Also known as: LNP* VERTON* Compound RFL-8036 Product reorder name: RVL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.69 | % | |
| Flow : 24 hr | 0.25 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 185 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 8900 | MPa | |
| 60°C | 7100 | MPa | |
| 100°C | 5800 | MPa | |
| 150°C | 5200 | MPa | |
| 200°C | 4800 | MPa | |
| Flexural Stress | ISO 178 | ||
| -- | 265 | MPa | |
| 60°C | 208 | MPa | |
| 100°C | 155 | MPa | |
| 150°C | 129 | MPa | |
| 200°C | 105 | MPa | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 3.3 | % | |
| 60°C | 3.9 | % | |
| 100°C | 4.0 | % | |
| 150°C | 3.6 | % | |
| 200°C | 3.4 | % | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C 3 | 15 | kJ/m² | |
| 23°C 4 | 16 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -40°C | 50 | kJ/m² | |
| 23°C | 54 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 258 | °C | ISO 75-2/Af |
| Specific Heat | 1850 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM D5930 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DynaPath™ 1910-SS | Polymer Dynamix | Nylon 6 | DynaPath™ |
| Egyeuroptene PP 5525 | Egyptian European Company | PP Homopolymer | Egyeuroptene |
| Hostacom X M3 T16 100000 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina BLACK PVC COMPOUND -E 60820-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETILEN F5-21T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |