Kapex C362
| Category: | PC , Polycarbonate |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Kapex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H5DdIu_Kapex-C362.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 % glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (1.60 mm) | 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 138 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7240 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 142 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.794 mm | HB | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoklar E01.10 C01010 | Ravago Group | PC | Sicoklar |
| UNITREX® Unfilled PEEK | Nytef Plastics, Ltd. | PEEK | UNITREX® |
| LG PMMA ID168 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| LNP™ STAT-KON™ WX06322 compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ CL002 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |