Laticonther 52/11 GR/70
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H4Rzt8_Laticonther-52-11-GR-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Polypropylene homopolymer (PPh). Graphite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.85 | % | |
| Flow : 2.00 mm | 0.45 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 25.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.60 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 20 | W/m/K | ASTM E1952-01 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 90 | ohms | ASTM D257 |
| Volume Resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV350LW 333 NER 4815 | Radici Plastics | Nylon 66 | Radilon® |
| Wellamid® GF14-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| GAPEX® HP RPP10EB91BK | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| INLUBE POMCCF10TF15 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INLUBE |
| Karina IVORY PVC COMPOUND 650D35/ 1-C-ISI-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |