duoMatrix®-G is a new three component polymer additive system that greatly enhances the physical properties of alpha gypsum products duoMatrix®-G (Matrix-G® for short) reduces the demold and drying time of gypsum and drastically reduces water permeability making it suitable for both interior and exterior applications (for exterior use, product must be sealed - see "post finishing" section). Matrix®-G has less odor and yields elements that are a brighter white than competing products. Matrix®-G is easy to use and can be cast solid, laid up by hand with chopped fiber or sprayed. Fully cured pieces can be painted, sanded, machined and polished. Matrix®-G is used to make lightweight pieces that are very strong and water-resistant. Applications include making architectural elements, reproducing sculpture and special effects. Vibrant colors are possible by adding pigments. Metal powders (bronze, pewter, brass, etc.) can be added to give the look of real metal castings at a fraction of the cost. You can duplicate the look of marble or ceramic by adding inexpensive fillers. Note: duoMatrix®-C is also available as a one component additive for concrete/GFRC (Glass Fiber Reinforced Concrete) applications.

Message

duoMatrix®-G is a new three component polymer additive system that greatly enhances the physical properties of alpha gypsum products duoMatrix®-G (Matrix-G® for short) reduces the demold and drying time of gypsum and drastically reduces water permeability making it suitable for both interior and exterior applications (for exterior use, product must be sealed - see "post finishing" section). Matrix®-G has less odor and yields elements that are a brighter white than competing products. Matrix®-G is easy to use and can be cast solid, laid up by hand with chopped fiber or sprayed. Fully cured pieces can be painted, sanded, machined and polished. Matrix®-G is used to make lightweight pieces that are very strong and water-resistant. Applications include making architectural elements, reproducing sculpture and special effects. Vibrant colors are possible by adding pigments. Metal powders (bronze, pewter, brass, etc.) can be added to give the look of real metal castings at a fraction of the cost. You can duplicate the look of marble or ceramic by adding inexpensive fillers.

Note: duoMatrix®-C is also available as a one component additive for concrete/GFRC (Glass Fiber Reinforced Concrete) applications.

General Information
Features	Good Strength Low to No Odor Low to No Water Absorption Machinable Paintable
Uses	Blending Modeling Material
Appearance	White
Processing Method	Casting Hand Lay-up Spraying

Physical	Nominal Value	Unit
Specific Volume	0.630	cm³/g

Additional Information	Nominal Value	Unit
Freeze/Thaw Resistance	3.0E+2	Cycles
Mixing Ratio	100 Parts Gypsum + 50 Parts C-1 Latex + 10 Parts C-2 Resin + 0.5 Parts C-3 Hardener

Physical	Nominal Value	Unit
Density	1.59	g/cm³
Water Absorption (24 hr)	0.25	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	22.8 to 37.9	MPa	ASTM D638
Flexural Strength	51.7 to 67.6	MPa	ASTM D790
Compressive Strength	44.8 to 65.5	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength	31	kJ/m²

Thermoset	Nominal Value	Unit
Pot Life	45 to 60	min
Demold Time	90 to 120	min

Resin Grade	Manufacturer	Category	Trademark
RTP 4005 SI	RTP Company	PPA	RTP
Quadrathane™ ALC-93A-B20	Biomerics, LLC	TPU-PC	Quadrathane™
Daelim Po1y® LD-41	DAELIM INDUSTRIAL CO., LTD.	LDPE	Daelim Po1y®
Ferro PP TPP20AT08NA	Ferro Corporation	PP, Unspecified	Ferro PP
WELLAMID Nylon 6600/58 GV 15 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 66	WELLAMID Nylon