EL-Pro™ P851JO
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H2xfNE_EL-Pro-P851JO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro P851JO is a general random copolymer polypropylene resin which has high clarity, high brightness, good processibility and contains anti-static agent suitable for injection molding process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 1.3 | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 31.4 | MPa | ASTM D638 |
| Fracture | 19.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 39 | J/m | ASTM D256 |
| 23°C | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | °C | ASTM D648 |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature | 150 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 84 | ASTM D2457 | |
| Haze | 9.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 25.0 - 70.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Injection Pressure: 40 to 80% of max. pressurePacking and Holding Pressure: 30 to 60% of max. pressureBack Pressure: 10% of max. pressure |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versalloy™ HC 9220-80 | PolyOne Corporation | TPE | Versalloy™ |
| Bergamid™ A700 TM-YF | PolyOne Corporation | Nylon 66 | Bergamid™ |
| APEX® 1335 | Teknor Apex Company | PVC, Flexible | APEX® |
| E-RIALFILL B 15 40 C | RIALTI Srl | PP, Unspecified | E-RIALFILL |
| LNP™ LUBRILOY™ UX98388 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |