TECAPEI™ TECAPEI™
| Category: | PEI , Polyether Imide |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAPEI™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H2gOkp_TECAPEI-TECAPEI-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in color, and combine exceptional mechanical, thermal, and electrical properties. The addition of glass fiber reinforcement in the 2000 series, coupled with Ensinger's proprietary extrusion techniques, provides the TECAPEI™ with both greater tensile strength and rigidity, while also improving dimensional stability. TECAPEI has many applications in medical, electronic/electrical, microwave, automotive, and aircraft industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2960 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 40 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 152 | MPa | ASTM D790 |
| Compressive Modulus | 3310 | MPa | ASTM D695 |
| Compressive Strength | 151 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 201 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(1.59 mm) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 2 | ASTM D149 | ||
| in Air | 33 | kV/mm | ASTM D149 |
| in Oil | 28 | kV/mm | ASTM D149 |
| Dielectric Constant 3(1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor 4(23°C, 1 kHz) | 1.3E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Additional Information |
|---|
| Data obtained from extruded shapes unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | 50% RH |
| 4 . | 50% RH, Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AG10NP | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Daelim Po1y® PP-137T | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| DINALON® B1X25 G30V0-4129 | Grupo Repol | Nylon 6 | DINALON® |
| Hylon® N2240MGHLUV | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| LNP™ THERMOCOMP™ EX00781H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |