Sup-tech A801

Category: Nylon 66 , Polyamide 66
Manufacturer: Shanghai Suptech Engineering Plastics Co. Ltd.
Trademark: Sup-tech
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: H274ir_Sup-tech-A801.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Sup-tech A801 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: impact modified.
General Information
Additive
  • Impact Modifier
Features
  • Impact Modified
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Density 1.08g/cm³DIN 53479
Molding Shrinkage 0.015 to 0.018%DIN 53464
Water Absorption DIN 53495
    23°C, 24 hr 1.2%
    Saturation, 23°C 6.7%
HardnessNominal ValueUnitTest Method
Rockwell Hardness (R-Scale)110ISO 2039-2
MechanicalNominal ValueUnitTest Method
Tensile Stress (Break)53.0MPaDIN 53455
Tensile Strain (Break)60%DIN 53452
Flexural Modulus 1500MPaDIN 53457
Flexural Stress 65.0MPaDIN 53457
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 80kJ/m²DIN 53453
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature DIN 53461
    0.45 MPa, Unannealed 190°C
    1.8 MPa, Unannealed 65.0°C
Melting Temperature 260°C
ElectricalNominal ValueUnitTest Method
Surface Resistivity 1.0E+13ohmsIEC 60093
Electric Strength 20kV/mmDIN 53481
InjectionNominal ValueUnit
Drying Temperature 90.0°C
Drying Time 6.0 to 10hr
Processing (Melt) Temp 255 to 285°C
Resin Grade Manufacturer Category Trademark
Manner Flexible PVC C8085 FR Manner Plastics, L.P. PVC, Flexible Manner Flexible PVC
Maxelast® P3908T Nantong Polymax Elastomer Technology, Co., Ltd TPE Maxelast®
KOPLA PA66 KDU1021 KOPLA Co., Ltd. Nylon 66 KOPLA PA66
Huafon JF-W-3012 Huafon Group Co., Ltd. PUR, Unspecified Huafon
Sylvin 9917-89 Black Sylvin Technologies Incorporated PVC, Unspecified Sylvin