RAMTAL PMH2017
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTAL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H1lT5w_RAMTAL-PMH2017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GENERAL PURPOSE POLYACETAL HOMOPOLYMER FOR INJECTION MOLDING APPLICATION,MFI 1.7. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 to 2.2 | % | ASTM D955 |
| -- | 1.8 to 2.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 72.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield) | 40 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 165 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-50D HF | RTP Company | TPV | RTP |
| RTP 209 RC HS Black | RTP Company | Nylon 66 | RTP |
| FHR EPS 54-S5454 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Hyril® GP355AS | Entec Polymers | SAN | Hyril® |
| LG ASA LI933 | LG Chem Ltd. | ASA | LG ASA |