InnoTuf® HP-1070A
| Category: | TSU-Ester , Polyurethane Thermoset Elastomer, Polyester Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H1MFpt_InnoTuf-HP-1070A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-1070A is a high performance 70 shore A polyester polyol based polyurethane formulated for hand-batch or meter mix processing methods. Excellent physical properties can be obtained with a post cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.14 | g/cm³ | |
| Cured | 1.15 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 1.0 to 1.5 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 4.00 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (Split) | 9.6 | kN/m | ASTM D470 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 48 Mix Ratio by Volume: 46 | ||
| Demold Time (66°C) | 60 to 180 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 43°C 1 | 0.70 | Pa·s | |
| 43°C 2 | 0.72 | Pa·s | |
| 43°C 3 | 0.73 | Pa·s | |
| Curing Time 4 | 1.8E+2 | hr | |
| Gel Time | 9.5 to 15 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 18.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 350 | % | ASTM D638 |
| Tear Strength | 35.0 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 16 hours at 150°F + 7 days at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALP 3511G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Chemical Resources ABS500 | Chemical Resources, Inc. | ABS | Chemical Resources |
| KOCETAL® GB706 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| RTP 699 X 143582 A | RTP Company | ABS | RTP |
| SABIC® LLDPE MG200024 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |