OmniPro™ CPP CCF10
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H11xQg_OmniPro-CPP-CCF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Calcium Carbonate Filled, Copolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Flexural Strength | 34.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 65.6 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® 935 NC010 | DuPont Performance Polymers | PET | Rynite® |
| Moplen HP483R | LyondellBasell Industries | PP Homopolymer | Moplen |
| MORETEC™ 0438CN | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| Trexprene® A40CW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| XENOY™ X2203 resin | SABIC Innovative Plastics | ABS+PBT+PC | XENOY™ |