Evoprene™ HP 3706
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ HP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H0WzUg_Evoprene-HP-3706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A range of high performance TPE compounds based on hydrogenated styrene block copolymer (H-SBC) specially formulated for applications requiring high strength and excellent abrasion resistance. Two ranges are offered, unfilled and filled. The unfilled versions offer the best properties with filled versions available as lower cost options Tensile strength for both types is mostly over 25% higher than comparable unfilled SEBS type compounds whilst DIN abrasion for all but the softest grades is two to three times better. The characteristic good compression set, heat ageing and low temperature properties are maintained whilst high levels of UV stability can be achieved with the correct choice of the appropriate masterbatch. For details please refer to our EvopreneTM General Information brochure. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 2782 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion | 52 | mm³ | DIN 53516 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| M-S Flow | 1.96 | MPa | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 1.90 | MPa | |
| 200% Strain | 2.60 | MPa | |
| 300% Strain | 3.40 | MPa | |
| Tensile Stress (Yield) | 9.50 | MPa | ISO 37 |
| Tensile Elongation (Break) | 550 | % | ISO 37 |
| Tear Strength 1 | 44 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 22°C, 72 hr | 22 | % | |
| 70°C, 22 hr | 35 | % | |
| 100°C, 22 hr | 48 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 to 190 | °C | |
| Middle Temperature | 160 to 190 | °C | |
| Front Temperature | 160 to 190 | °C | |
| Nozzle Temperature | 160 to 190 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G27 NTLA010 NR364 MSM | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Adsyl 7572 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Grilamid® LV-30H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LNP™ STAT-KON™ DX09303C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ RZ0069 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |