LEXAN™ FXG1414T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzUDqX_LEXANFXG1414Tresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-siloxane copolymer in special "Diamond Sparkle" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.40 - 0.80 | % | Internal method |
| Flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.13 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2060 | MPa | ASTM D638 |
| -- | 2250 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 58.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 45.0 | MPa | ASTM D638 |
| Fracture | 49.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 5.7 | % | ASTM D638 |
| Yield | 5.4 | % | ISO 527-2/50 |
| Fracture 6 | 52 | % | ASTM D638 |
| Fracture | 11 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2230 | MPa | ASTM D790 |
| -- 8 | 2150 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 88.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 350 | J/m | ASTM D256 |
| 23°C | 520 | J/m | ASTM D256 |
| -30°C 11 | 20 | kJ/m² | ISO 180/1A |
| 23°C 12 | 32 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 49.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 121 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 118 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ASTM D1525 14 |
| -- | 140 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 95°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 95°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 217 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71.0 - 93.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-88S | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| Sumikon® VM 1712L17D | Mitsubishi Chemical Corporation | PVC, Rigid | Sumikon® VM |
| Sylvin 86025-38DUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TF3CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Hostacom BA16G | LyondellBasell Industries | PP Copolymer | Hostacom |