Xuchuan A-7150/B-8260
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gz3Uou_Xuchuan-A-7150-B-8260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan A-7150/B-8260 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Applications of Xuchuan A-7150/B-8260 include consumer goods and marine applications. Primary characteristic: low temperature resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.550 to 0.700 | g/cm³ | |
| Density | |||
| A-7150 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-8260 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-7150 : 40°C | 1.00 to 1.40 | Pa·s | |
| B-8260 : 40°C | 0.700 to 1.10 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Ross Flex (-20°C) 1 | No Crack |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 9.0 to 11.0 | sec | |
| End of Rise Time | 1.0 to 1.2 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 250 to 300 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 8.0 to 12.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 to 65 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 9.50 to 13.0 | MPa | |
| Tensile Elongation (Break) | 500 to 750 | % | |
| Tear Strength | 38.0 to 50.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 94 to 95 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Note Message | |
|---|---|
| 1 . | 40000 cycles, Break length 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E-200GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Ultramid® 66 H2 G/25-V0KB1 NAT0046 | BASF Corporation | Nylon 66 | Ultramid® |
| Comtrex Flexible PVC® 97CF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| Karina IVORY PVC COMPOUND -E 90900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lusin® Clean LD 250 | Chem-Trend L.P. | Unspecified | Lusin® |