3M™ Dyneon™ PTFE Compound TF 6221
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GyuwUQ_3M-Dyneon-PTFE-Compound-TF-6221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.14 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.63 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 3.0 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 64 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 27.0 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 280 | % | ASTM D4745-06 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+4 | ohms·cm | IEC 60093 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 35.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® EL700 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| TITANPRO® L-670M | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| TOTAL Polypropylene PPH 3273 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| DILAMID® 66 FV NATURAL 2808 | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| KMI PP KM-003IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |