Resilience™ LS22000M
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GycGB6_ResilienceLS22000M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Custom Molding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Spiral Flow | 104 | cm | |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 3.18 mm) | 1910 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C, 3.18 mm) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm) | 35 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 1920 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 57.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 210 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 59.5 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 67.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 51.6 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 64.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 51mm/min |
| 2 . | Type 1, 51mm/min |
| 3 . | Type 1, 51mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beamset AQ-9 | Arakawa Chemical Industries, Ltd. | Epoxy | Beamset |
| Fortron® 6165A4 | Celanese Corporation | PPS | Fortron® |
| Kingfa PBT G30 | Kingfa | PBT | Kingfa PBT |
| DEXFLEX® 727-UV 4LLA | LyondellBasell Industries | PP, Unspecified | DEXFLEX® |
| Sylvin 916VO-85 White 1481 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |