LNP™ THERMOCOMP™ NX10302 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GyKctn_LNP-THERMOCOMP-NX10302-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This is a PC/ABS compound with improved plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.65 | % | |
| Across Flow : 24 hr | 0.50 to 0.56 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.010 | % | |
| 24 hr, 50% RH | 0.020 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2480 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 46.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 4.2 | % | |
| Break | 100 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2400 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 80.0 | MPa | |
| Break, 50.0 mm Span | 79.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 108 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1.00 GHz) | 2.74 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 3.0E-3 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 100 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 290 | °C | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESNO P20 TLO | Arkema | Nylon 11 | Rilsan® |
| Adell Polyamide AR-67 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| ARC ARC60G13 | ARC Resin Corporation | Nylon 6 | ARC |
| Gallonprene® GP520-4009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Latistat 47/7-03 | LATI S.p.A. | PP Copolymer | Latistat |