| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gwy74V_AEI-SX408-CM401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Silane crosslinkable polyethylene for medium voltage power cable insulation This is a silane crosslinkable polyethylene compound, curable by exposure to moist conditions and possessing excellent extrusion properties at high output rates. The graft component SX408 is mixed with a crosslinking catalyst masterbatch CM401 generally in the ratio 95:5. The SX408:CM401 compound has been specifically developed for cables operating up to 36kV. This compound is typically used in conjunction with SX 539 crosslinkable semi-conducting material for conductor and insulation shields. Strippable outer shields are possible using SX528. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | BS 2782 620A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 18.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 350 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | 4.0 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break (135°C, 168 hr) | -2.0 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Bend (-70°C) | pass | IEC 60811-1-4 | |
| Thermosetting- Elongation under load, 20N/cm² 1(200°C) | % | IEC 60811-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor- 50Hz (23°C) | 4.00E-4 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | > 1.0E+16 | ohms·cm | IEC 60502 |
| Dielectric Strength (20°C) | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 50 Hz) | 2.20 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Die Temperature | 180 | °C |
| Extrusion instructions |
|---|
| Most modern thermoplastic extruders will process SX408:CM401 compounds particularly if a screw suitable for polyethylene extrusion is available. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1503-55D | RTP Company | TEEE | RTP |
| ULTEM™ JD7904 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| DAI-EL™ G-501NK | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina COMP. PVC CRYSTAL -E 60/264-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina COMP. PVC CRYSTAL -E 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |