Trexprene® A67CW
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GwezRH_Trexprene-A67CW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A67CW is a pre-colored, heat and UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). It is primarily intended for Exterior applications where a pre-colored compound with good compressions set and UV properties are needed. This pre-colored material can be processed using Extrusion, Injection, or Blow Molding equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 to 1.01 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 62 to 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 2.50 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 7.10 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 630 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 34 | kN/m | ISO 34-1 |
| Compression Set | |||
| 125°C, 70 hr | 44 | % | ASTM D395B |
| 125°C, 70 hr 5 | 44 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 1000 hr) | -17 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (135°C, 1000 hr) | -13 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Duration 6 | Delta E < 3 | SAE J2527 | |
| Ozone Resistance 7(40°C) | 0 Rating | ISO 1431-1 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Extended UV Filters, 2500 kJ/m 2 |
| 7 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 33 GF NAT | RTP Company | Nylon 66 | RTP |
| Toppyl SP 2101 C | LyondellBasell Industries | PB | Toppyl |
| EMPILON® 545 | EMPILON | SEBS | EMPILON® |
| LG PMMA EG920B | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Sylvin 9710-80FUV Red 6228 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |