GLS Nylon 6 PN09 IM1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GviQbs_GLS-Nylon-6-PN09-IM1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon6 Impact Modified Precolor |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 to 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | > 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 8.0 | % | ASTM D638 |
| Flexural Modulus 3 | > 1600 | MPa | ASTM D790 |
| Flexural Strength 4 | > 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 56.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 180 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 278 | °C | |
| Mold Temperature | 55.0 to 95.0 | °C | |
| Injection Pressure | 68.0 to 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -M M5002D | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| Toyolac® 325 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| BMC 3001 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Kemcor LD 1492 | Qenos Pty Ltd | LDPE | Kemcor |
| HIPOLEN P® FL 5 | Hipol a.d. | PP Homopolymer | HIPOLEN P® |