RELENE® 46GP003
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GvEqCd_RELENE-46GP003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Relene 46GP003 (PE-100) is a natural colored grade for pipe extrusion. It possesses bimodal molecular weight distribution, which improves processability. This grade meets the MFI, Density & Hydrostatic strength requirements of material grade PE-100 as per IS: 4984. When incorporated with adequate quantity of carbon black as specified in clause 5.2.3 of IS: 4984, pipes will meet PE:100 requirements. Pipes made from Relene 46GP003 grade passes the Internal Pressure Creep Rupture Test when tested with 5.5 MPa induced stress at 80°C for 165 hrs and with 5.7 MPa induced stress at 80°C for 48 hrs as per clause 8.1 of IS 4984, thereby meeting the requirements of PE100 grade. The grade conforms to ISO 4427 specification shown and has been certified for MRS> 10MPa as per ISO 9080. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.30 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | > 600 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 850 | MPa | ASTM D790 |
| Hydrostatic Pressure Test | ISO 1167 | ||
| 20°C 1 | > 4.2 | day | |
| 80°C 2 | > 41.7 | day | |
| 80°C 3 | > 6.9 | day |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 30 | min | ASTM D3985 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS | > 10.0 | MPa | ISO 9080 |
| SCG | > 20.8 | day | ISO 13479 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | No Break | ASTM D256 |
| Note Message | |
|---|---|
| 1 . | 12.4 MPa |
| 2 . | 5 MPa |
| 3 . | 5.4 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEZ-250 | SHIN-A T&C | Epoxy | SHIN-A |
| THERMOLAST® M TM0HET (Series: MC/HE) | KRAIBURG TPE | TPE | THERMOLAST® M |
| Badaflex® TPE-S 45A 1000LD | Bada AG | TPE | Badaflex® |
| EnCom F0 GF20 PC | EnCom, Inc. | PC | EnCom |
| Sylvin 8366-88C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |