KPOL-HDPE HD K-0.35/955 BO

Category:	HDPE , High Density Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Gum58L_KPOL-HDPE-HD-K-0-35-955-BO.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene Copolymer 1-hexene Extrusion-Blow Molding

Applications

Bottles for home use chemical liquid substances (bleache) and industrial chemicals (lubricants) up to 10 litters.

Bottles containing liquids for personal use (shampoo). Bottles for pharmaceutical products.

Characterisitics

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant Optical Whitener
Features	Antioxidant Copolymer Food Contact Acceptable Hexene Comonomer High Density
Uses	Bottles Pharmaceuticals
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.955	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.35	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
Condition B, 60°C, 10% Igepal CO-630, F50 ¹	> 500	hr	ASTM D2561
50°C, 3.18 mm, 100% Igepal CO-630, F50 ²	45.0	hr	ASTM D1693A
50°C, 1.91 mm, 100% Igepal CO-630, F50 ³	35.0	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	67		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ⁴(Yield)	27.6	MPa	ASTM D638
Tensile Elongation ⁵(Break)	600	%	ASTM D638
Flexural Modulus - Tangent ⁶(3.20 mm)	1380	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact ⁷(3.20 mm)	270	J/m	ASTM D256A
Tensile Impact Strength	242	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁸(0.45 MPa, Unannealed)	76.0	°C	ASTM D648
Brittleness Temperature ⁹	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	127	°C	ASTM D1525 ¹⁰
Melting Temperature	129	°C	DSC

Note Message
1 .	16 oz cylindrical bottle (approximated mass of 20 g) filled up to 33% of its capacity
2 .	Grooved Specimen
3 .	Grooved Specimen
4 .	Type IV, 50 mm/min
5 .	Type IV, 50 mm/min
6 .	13 mm/min
7 .	Muesca
8 .	2°C/min
9 .	F50; 25 lbfXin
10 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RapidCast™ RC-255	Innovative Polymers, Inc.	TSU	RapidCast™
Sup-tech B706	Shanghai Suptech Engineering Plastics Co. Ltd.	Nylon 6	Sup-tech
ALTECH® PA6 C 3230/100 GB20 GF10	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6
Fainplast PVC PMS 60	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
HydroMed™ D4	AdvanSource Biomaterials Corp.	PUR-Ether	HydroMed™