ENVIROPLAS® ENV08-NC830
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GtWm7V_ENVIROPLAS-ENV08-NC830.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compounding - Injection Molding Grade, Excellent Processability, Good Chemical and Heat Resistance, Good Surface Appearance, Low Thermal Expansion, Outstanding Wear and Friction Performance. NC830 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV08 Series Products Are Available With Mold Release and/or UV Stabilizer. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 51 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 2320 | MPa | ASTM D790 |
| Flexural Strength | 81.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 151 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 50.6 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 216 to 238 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 221 to 243 | °C | |
| Nozzle Temperature | 216 to 238 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rigidex® HD6070EA | INEOS Olefins & Polymers Europe | HDPE | Rigidex® |
| Hapflex™ 671-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Karina BLUE PVC COMPOUND 902-06/595-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJ'ECO DFRG178G - 1199 | AD majoris | Biodeg Polymers | MAJ'ECO |
| MAXATEL® AH100ST-BK | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |