CALIBRE™ IM 401-18
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GsqvB5_CALIBRE-IM-401-18.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ IM 401-18 Impact Modified Polycarbonate resins is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy processing with improved impact strength in highly filled formulations. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1190 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 15.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955, ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield 4 | 57.9 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Yield | 60.0 | MPa | ISO 527-2 5 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2 6 |
| Break 7 | 110 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 8 |
| Flexural Modulus | |||
| -- 9 | 2280 | MPa | ASTM D790 |
| -- | 2270 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 10 | 89.6 | MPa | ASTM D790 |
| -- | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 11 | ||
| -30°C | 30.0 | kJ/m² | |
| 23°C | 60.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 12 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256, ISO 180/4A |
| Instrumented Dart Impact 13(23°C, Total Energy) | 50.8 | J | ASTM D3763 |
| Tensile Impact Strength | 588 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa | 134 | °C | ISO 75-2 14 |
| 1.8 MPa, Unannealed | 121 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 136 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa | 119 | °C | ISO 75-2 15 |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ASTM D1525, ISO 306/B50 9 16 |
| 50°C/h, B (50N) | 140 | °C | ISO 306 17 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 18 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 19 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | V-2 | ISO 1210 20 | |
| Burning Behav. at thickness h (3.20 mm, UL) | V-2 | ISO 1210 21 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | 50 mm/min |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 50 mm/min |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Method I (3 point load), 2.0 mm/min |
| 10 . | Method I (3 point load), 2.0 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | 3.39 m/sec |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Rate A (50°C/h), Loading 2 (50 N) |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA666G33HS1L-BK10 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| Reon 67GER01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Teflon® PTFE DISP 30 | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Tool-A-Thane UT-405 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Topolymer® 6231-H/G | Dongguan Top Polymer Enterprise | TPE | Topolymer® |