Terblend® N NG-04
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terblend® N |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GspWn5_Terblend-N-NG-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terblend N NG-04 is a 20% glass fiber reinforced ABS/PA blend with high dimensional stability and rigidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 107 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.2 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 3.2 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 164 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ISO 306/A50 |
| -- | 114 | °C | ISO 306/B50 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.013 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restramid PA 6 30GF/V0 | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| UBE Nylon 7024 B | UBE Engineering Plastics, S.A. | Nylon 612 | UBE Nylon |
| Kumho EPS GN20 HC | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Kepamid® 2350GB | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ THERMOTUF™ WF006I compound | SABIC Innovative Plastics | PBT | LNP™ THERMOTUF™ |