Syncure™ System S107FH
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GspIQm_Syncure-System-S107FH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Forms of UL certification approved: 3167, 3168, 3173, 3182, 3195, 3196, 3226-3229, 3238, 3290, 3295-3298, 3300, and 3457. |
| General Information | |
|---|---|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Gel Content 1 | 72 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention rate 2(158°C, 1.91 mm) | 75 | % | |
| Elongation retention rate 3(158°C, 1.91 mm) | 75 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture- V-0045G RoHS | 33 | % | |
| Transplant-based resin- S-1054A | 67 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 64 | ASTM D2240 | |
| Shaw D, 10 seconds | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 5(Break) | 400 | % | ASTM D638 |
| Deformation Under Load (131°C) | 10.0 | % | UL 1581 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| UL Temperature Rating | 125 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 注释：以上情况代表了在30密耳壁的18 AWG上测量得出的典型属性。存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | 672 hours, UL standard |
| 3 . | 672 hours, UL standard |
| 4 . | Type 4, 510mm/min |
| 5 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| SOLPLAST TC 3000D | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| HAIPLEN H30 G2 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| HiFill® PA6/6 GF15 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LG ABS SG175G | LG Chem Ltd. | ABS | LG ABS |