PRL ABS-G5
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GsWPXF_PRL-ABS-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL ABS-G5 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 5.0% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.50 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 45.5 | MPa | |
| Break, 3.18 mm | 42.7 | MPa | |
| Flexural Modulus (3.18 mm) | 2900 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 93.3 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 87.8 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 191 to 199 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 210 to 227 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 48.9 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A34100 H | 4Plas | Nylon 66 | 4MID® |
| CP PRYME® Polycarbonate PC300R | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| DAI-EL™ G-723F | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |
| Daelim Po1y® TR-147 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| KRATON® A1536 H | Kraton Polymers LLC | SEBS | KRATON® |