Quantum Composites QC-8800
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | Quantum Composites Inc. |
| Trademark: | Quantum Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GsFQDb_Quantum-Composites-QC-8800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| QC-8800 is a vinyl ester based sheet molding compound (SMC) designed for compression molding of components requiring high structural strength. It exhibits unusual toughness, and is suggested for applications subject to impacts and rough handling. QC-8800 is also suggested for applications requiring excellent fatigue resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.90 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 70 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 26200 | MPa | ASTM D638 |
| Tensile Strength | 345 | MPa | ASTM D638 |
| Flexural Modulus | 20700 | MPa | ASTM D790 |
| Flexural Strength | 586 | MPa | ASTM D790 |
| Compressive Modulus | 18600 | MPa | ASTM D695 |
| Compressive Strength | 290 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 1900 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| CLTE - Flow | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 12 | kV/mm | ASTM D149 |
| Arc Resistance | 129 | sec | ASTM D495 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life | |||
| 4°C | 52 | wk | |
| 24°C | 8.7 | wk | |
| Demold Time (138°C) | 3.0 to 5.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 132 to 149 | °C | |
| Injection Pressure | 1.38 to 6.89 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1010 PA1010 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1010 | Shandong PA1010 |
| Ultrathene® UE637000 | LyondellBasell Industries | EVA | Ultrathene® |
| ARMAMID® PA 6-1UP | Poly Plastic | Nylon 6 | ARMAMID® |
| Teldene® H08ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| KOPPS® S23G40BL | Kolon Plastics, Inc. | PPS | KOPPS® |