Formlabs Clear
| Category: | Unspecified , Unspecified |
| Manufacturer: | Formlabs Inc. |
| Trademark: | Formlabs |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gs58lW_Formlabs-Clear.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Formlabs CLEAR resin produces strong plastic parts ideal for a wide variety of applications and is specifically designed to work with your Form 1+ 3D Printer. This material can be easily painted, and when the surface is finished or coated, produces a highly clear part. Upon post-cure, tensile strength and stiffness exceeds that of injection-molded or 3D-printed ABS. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- 2 | 1300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 3 | 61.5 | MPa | ASTM D638 |
| Yield 4 | 29.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 5 | 5.0 | % | ASTM D638 |
| Fracture 6 | 20 | % | ASTM D638 |
| Flexural Modulus | ASTM D790A | ||
| -- 7 | 2380 | MPa | ASTM D790A |
| -- 8 | 970 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 9 | 29 | J/m | ASTM D256 |
| -- 10 | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed 11 | 78.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed 12 | 52.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 13 | 60.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 14 | 47.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Material properties can vary with part geometry, print orientation, print settings and temperature. |
| Note Message | |
|---|---|
| 1 . | After exposing green parts to 15 J/cm² of UV light. |
| 2 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 3 . | After exposing green parts to 15 J/cm² of UV light. |
| 4 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 5 . | After exposing green parts to 15 J/cm² of UV light. |
| 6 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 7 . | After exposing green parts to 15 J/cm² of UV light. |
| 8 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 9 . | After exposing green parts to 15 J/cm² of UV light. |
| 10 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 11 . | After exposing green parts to 15 J/cm² of UV light. |
| 12 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| 13 . | After exposing green parts to 15 J/cm² of UV light. |
| 14 . | Data was obtained from green parts, printed using 50 µm Clear settings, without additional treatments. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HNR101 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Xuchuan 2020/B-8020 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| APEX® 130 | Teknor Apex Company | PVC, Flexible | APEX® |
| Sylvin 8999-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 60 EF DUS097 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |