Zytel® RS LC4601 BK010
| Category: | Nylon, Unspecified , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GrwGBX_ZytelRSLC4601BK010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plasticized, Toughened, Renewably Sourced, Polyamide Developed for Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.03 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.3 | -- | % | ISO 294-4 |
| Flow | 1.6 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 750 | 470 | MPa | ISO 527-2 |
| Tensile Stress (50% Strain) | 33.0 | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | ||||
| Fracture | > 50 | > 50 | % | ISO 527-2 |
| Fracture, 23°C | 300 | -- | % | ISO 527-2/50 |
| Flexural Modulus | 720 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 100 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 15 | -- | kJ/m² | ISO 180/1A |
| 23°C | 84 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 53.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 50.0 | 30.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 213 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Extrusion Melt Temperature, Optimum | 235 | °C |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (280°C, 1000 sec^-1) | 190000 | -- | mPa·s | ISO 11443 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.060 | % | |
| Melt Temperature | 230 - 245 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 A4G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Sinvicomp SGH5000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TEREZ ABS 5010 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| UNISOFT TPE™ ST-60A-BK-4-02 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Eltex® Superstress™ CAP508S2 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |