Radilon® A VHS 338 M NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GrYNnG_Radilon-A-VHS-338-M-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 injection moulding grade. Nucleated for fast cycles. Black colour. Suitable for parts requiring high productivity. Specifically developed for automotive head light bezels. ISO 1043 : PA66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 8.9 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3400 | 3100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 88.0 | 55.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | -- | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 5.0 | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 3100 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 120 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 12 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 800 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxiglas® MG515 | Maxiglas Corporation | Acrylic (PMMA) | Maxiglas® |
| Okirol® E-6 | DIOKI d.d. | PS (EPS) | Okirol® |
| PENTAMID A GV30 H TF15 schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Rotuba CAB B9004 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| Sylvin 8699-75 Clear Blue 8434 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |