WPP PP PPH3GF3-UV Black
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GqxMDV_WPP-PP-PPH3GF3-UV-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Properties shown below for this filled blend are typical for a 30% fiberglass reinforced polypropylene compound. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 89.6 | MPa | ASTM D638 |
| Flexural Modulus - Secant 2 | 5990 | MPa | ASTM D790 |
| Flexural Strength 3 | 154 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 13 mm/min |
| 3 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2950 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 399 X 134920 A | RTP Company | PC | RTP |
| Tuftec™ M1911 | AKelastomers | SEBS | Tuftec™ |
| CERTENE™ LLHF-116XF | Muehlstein | LLDPE | CERTENE™ |
| EXCELLEN® GMH CB1001 | Sumitomo Chemical Asia | PE, Unspecified | EXCELLEN® GMH |