Vyncolit® BXE7670
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gqk6Oq_Vyncolit-BXE7670.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® BXE7670 is a glass fiber reinforced phenolic molding compound with excellent mechanical properties and high temperature resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.84 | g/cm³ | ISO 1183 |
| Apparent Density | 0.59 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.14 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.2 | % | ISO 178 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | >PF-(GF+GB+MD)65< | ISO 11469 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 19000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 101 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.68 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 18000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 210 | MPa | ISO 178 |
| Compressive Stress | 293 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 14 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed 1 | > 250 | °C | ISO 75-2/Af |
| 1.8 MPa, Unannealed | 223 | °C | ISO 75-2/Af |
| 8.0 MPa, Unannealed 2 | > 250 | °C | ISO 75-2/Cf |
| 8.0 MPa, Unannealed | 171 | °C | ISO 75-2/Cf |
| CLTE | ASTM E831 | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 5.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.45 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.7E+13 | ohms | IEC 60093 |
| Volume Resistivity | 4.2E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | postcured up to 210°C |
| 2 . | postcured up to 210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTAL PM1009 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| TEREZ PMMA 5001 | TER HELL PLASTIC GMBH | Acrylic (PMMA) | TEREZ PMMA |
| Hanwha Total PP FB54NH | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LUVOCOM® 90-8553 | Lehmann & Voss & Co. | HDPE | LUVOCOM® |
| Dryflex® SE 40A201 | ELASTO | TPE | Dryflex® |