NYCOA Polyamide 2076
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GqWpN9_NYCOA-Polyamide-2076.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2076 is a high viscosity resin particularly suitable for extrusion processing. Its high melt viscosity and extremely good melt strength provides ease of processing for tubing, complex profile, and mandrel extrusion. NYCOA 2076 was specifically formulated to offer higher flexibility, higher strength, and very high impact toughness, in large diameter extruded products. The high melt strength prevents ripples or necking in mandrel extrusion. Typical extrusion applications include hose mandrels for rubber vulcanization, high-pressure & hydraulic hoses, and flexible & vacuum tubing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.80 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 34.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 124 | MPa | ASTM D790 |
| Flexural Strength 4 | 6.89 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | No fracture 690 J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 205 | °C | DSC |
| Additional Information |
|---|
| Tensile Elongation at Break, ASTM D638, 2 in/min: 500+%The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CF60LA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| DURACON® EX-09 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| apilon 52® FA-7505 | API SpA | TPU-Polyester | apilon 52® |
| OTECH TPR OTR4005-Soles | OTECH Corporation | TPE | OTECH TPR |
| Sylvin 9067-90 LMW Grey 9368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |