Lucel® HI510
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GqRYLe_Lucel-HI510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUCEL HI-510 is high impact strength grade added with impact modifiers.LG chemical supplies a wide range of grades depending on the types and contents of modifiers to meet the requirement of our customers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.7 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 54.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 90 | % | ASTM D638 |
| Flexural Modulus 2 | 1880 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 65.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 | |
| Reverse Notch Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 150 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C | |
| CLTE - Flow (20 to 80°C) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Melt Temperature (Aim) | 190 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 68.6 to 118 | MPa | |
| Back Pressure | 3.92 to 7.84 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 15 mm/min |
| 3 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 GF 30I | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Zythane® 4080A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Honeywell Halar E500 | Honeywell | PCTFE | Honeywell Halar |
| Hylex® P1318FRVNHE | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| LNP™ THERMOCOMP™ MF006AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |