Formolene® HP4306
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GpySC9_Formolene-HP4306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Density Hexene Copolymer Formolene HP 4306 is a high performance copolymer that is designed for the most demanding requirements of pressure pipe applications. It is designed specifically for larger diameter and thick wall pipes where excellent melt strength is required, but can be used successfully on all diameters and wall thicknesses. It has good long-term hoop strength performance, very high melt strength, outstanding toughness even at low temperatures. Formolene HP 4306 meets all requirements of ASTM D4976 - PE 235. When blended with the approved color concentrates, Formolene HP4306 has a cell class of 345464C per ASTM D3350-05, is listed by PPI as a PE3608 material with HDB's of 1,600 psi @ 73°F and 800 psi @ 140°F and meets the requirements of NSF Standard 14/61 for use with potable water. HP4306 also qualifies as a PE3408 material under the old ASTM D3350-02a and PPI standards. HP4306 also qualifies as a PE80 material per ISO 9080. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| -- 1 | 0.944 | g/cm³ | |
| -- 2 | 0.955 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg 3 | 0.060 | g/10 min | |
| 190°C/21.6 kg 4 | 8.0 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| 100% Igepal, Compression Molded, F50 | > 1000 | hr | ASTM D1693A |
| 100% Igepal, Compression Molded, F50 | > 1000 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | > 1000 | hr | ASTM D1693C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5 | ASTM D638 | ||
| Yield, Compression Molded | 22.1 | MPa | |
| Break, Compression Molded | 34.5 | MPa | |
| Tensile Elongation 6(Break, Compression Molded) | > 500 | % | ASTM D638 |
| Flexural Modulus | |||
| Compression Molded | 758 | MPa | ASTM D3350 |
| Compression Molded | 965 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| PENT - slow crack growth | 150 | hr | ASTM F1473 |
| Note Message | |
|---|---|
| 1 . | Natural |
| 2 . | Black |
| 3 . | MI |
| 4 . | HLMI |
| 5 . | Type IV, 51 mm/min |
| 6 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5286 Polyol/ 5286 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| THERMOLAST® K TC6HAA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Badamid® LA70 GF50 H MoS2 1% | Bada AG | Nylon 66 | Badamid® |
| Baoding 76T85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| ASTALAC™ ABS KMZ | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |