NORYL™ PX9406P resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GpZIK3_NORYL-PX9406P-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 125dc HDT. UL94 V-0 rated. Electrical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| -- | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 3.9 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/10.0 kg | 27.0 | cm³/10min | |
| 280°C/5.0 kg | 10.0 | cm³/10min | |
| 300°C/5.0 kg | 23.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 63.0 | MPa | Internal Method |
| Yield | 73.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 85 | % | Internal Method |
| Break | 4.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2350 | MPa | ASTM D790 |
| -- 1 | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 99.0 | MPa | ASTM D790 |
| -- | 108 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(-30°C) | 9.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| -40°C 4 | 8.0 | kJ/m² | ISO 180/1A |
| -30°C 5 | 8.0 | kJ/m² | ISO 180/1A |
| -20°C 6 | 9.0 | kJ/m² | ISO 180/1A |
| -10°C 7 | 10 | kJ/m² | ISO 180/1A |
| 0°C 8 | 11 | kJ/m² | ISO 180/1A |
| 23°C 9 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 136 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 131 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 117 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A120 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test 12(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -30 to 30°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.80 | ||
| 60 Hz | 2.80 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.750 mm | V-0 | ||
| 2.50 mm | 5VA |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (280°C, 1500 sec^-1) | 278 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| 12 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GV 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Mylar® WC (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| CYCOLOY™ CM6140 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| HIPOL™ L840 | Mitsui Chemicals, Inc. | PP, Unspecified | HIPOL™ |
| Laser+® C 61803 (E67A) | DAK Americas LLC | PET | Laser+® |