| Unfilled NORYL Classico grade with high RTI rating (125 oC) |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/5.0 kg | 8.00 | cm³/10min | |
| 300°C/5.0 kg | 20.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 72.0 | MPa | ASTM D638 |
| Yield | 71.0 | MPa | ISO 527-2/50 |
| Break | 57.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 6.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Break | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 100 mm Span 3 | 2580 | MPa | ASTM D790 |
| -- 4 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 100 mm Span 5 | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 220 | J/m | ASTM D256 |
| -40°C 6 | 8.0 | kJ/m² | ISO 180/1A |
| -30°C 7 | 8.0 | kJ/m² | ISO 180/1A |
| -20°C 8 | 10 | kJ/m² | ISO 180/1A |
| -10°C 9 | 11 | kJ/m² | ISO 180/1A |
| 0°C 10 | 12 | kJ/m² | ISO 180/1A |
| 23°C 11 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 123 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A120 |
| -- | 144 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 1.50 mm | 825 | °C | |
| 2.00 mm | 825 | °C | |
| 3.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP513-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Tenite™ Butyrate 530E3720010 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Sylvin 2953-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX674PC resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| NYLOY® MG-1014NM | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |