SABIC® Vestolen A 5017
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Go4tGr_SABIC-Vestolen-A-5017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®Vestolen A 5017 is a high-density polyethylene product,. It can be processed by injection molding and is available in Europe. SABIC®Vestolen A 5017 applications include hats/caps/corks, containers and food contact applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 10 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 28 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 60 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 49.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1050 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 23.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 500 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 530 | MPa | ISO 899-1 |
| 1000 hr | 240 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 3.8 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 36.0 | kJ/m² | ISO 8256/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 47.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 128 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >500%ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 40hrTensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.6%Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 34 MPaMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 131°CEnthalpy Change, DIN 53765: 206J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CF75CB | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Caltex PP H430 | GS Caltex | PP Homopolymer | Caltex PP |
| LEXAN™ ML7664 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ THERMOCOMP™ LX03447 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| LUVOCOM® 1105-8174 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |