Order Products : sales@su-jiao.com
Hypel® PEHD.7/.962
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Entec Polymers |
| Trademark: | Hypel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gnu4bN_Hypel-PEHD-7-962.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hypel® PEHD.7/.962 is a High Density Polyethylene material. It is available in North America. Important attributes of Hypel® PEHD.7/.962 are:
Typical application of Hypel® PEHD.7/.962: Food Contact Applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.962 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 31.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 400 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1550 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.35 mm) | 81.7 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LDPE XL700 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| TECHNYL® 2912GMH7-P BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Huafon JF-D-NC8905 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| InnoPlus HD2408J | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Karina CLEAR PVC COMPOUND 74/203-D-IS-SI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |