Lucofin® 1400SL

Category:	EBA , Ethylene Butyl Acrylate Copolymer
Manufacturer:	Lucobit AG
Trademark:	Lucofin®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GnGgfh_Lucofin-1400SL.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Lucofin® 1400SL is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin® 1400SL is softer and more flexible than ethylene homopolymeres with comparable density. Lucofin® 1400SL is supplied as uncoloured granules. The product contains slip agent.

Lucofin® 1400SL is used as component in multi-layer film constructions or as a polymer modifier to improve splitting resistance, environmental stress crack resistance ESCR, resistance to low temperatures, weldability, and processability.

Product advantages

flexibility

impact strength at low temperatures (- 40°C)

thermal stability of polymer (no corrosive by products)

good mechanical properties

high end use temperature

good compatibility and filler acceptance

good organoleptics

environmentally sound

General Information
Additive	Slip
Features	Acid Resistant Base Resistant Copolymer Environmentally Sound Good Flexibility Good Organoleptic Properties Good Processability Good Thermal Stability High ESCR (Stress Crack Resist.) Low Temperature Impact Resistance Salt Water/Spray Resistant Slip Soft Weldable
Uses	Agricultural Applications Blow Molding Applications Coating Applications Film Plastics Modification Profiles Sheet
Appearance	Natural Color
Forms	Granules
Processing Method	Extrusion Blow Molding Film Extrusion Injection Molding Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.924	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.4	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore A)	90		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	62.0	MPa	ISO 527-2
Tensile Stress (Yield)	4.00	MPa	ISO 527-2
Tensile Strain (Yield)	15	%	ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	70.0	°C	ISO 306/A50
Melting Temperature (DSC)	96.0	°C	ISO 3146

Additional Information	Nominal Value	Unit	Test Method
Comonomer BA	16	%	DIN 51451

Injection	Nominal Value	Unit
Processing (Melt) Temp	180 to 250	°C
Mold Temperature	10.0 to 40.0	°C

Extrusion	Nominal Value	Unit
Melt Temperature	160 to 230	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 1381	RTP Company	PPS	RTP
Viprene™ G60A-32U-NAT	Alliance Polymers & Services	TPV	Viprene™
3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4212	3M Advanced Materials Division	PTFE	3M™ Dyneon™ TFM™ Modified PTFE Compound
Plaslube® J-4/30/TF/13/SI/2 NAT	Techmer Engineered Solutions	Nylon 612	Plaslube®
PlexTuf L-66119	Altuglas International of Arkema Inc.	Acrylic (PMMA)	PlexTuf