CALIBRE™ 301-9
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GnEesM_CALIBRE-301-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 301-9 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 71.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2410 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 96.5 | MPa | ASTM D790 |
| -- 9 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D256 |
| 23°C | 90 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 10(23°C, Total Energy) | 87.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 144 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 149 | °C | ISO 306/B50, ASTM D1525 11 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 12 | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index 13 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Method I (3 point load), 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 3.39 m/sec |
| 11 . | Rate A (50°C/h), Loading 2 (50 N) |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraypef® 25020 AP17 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| EVICOM™ GD1/774 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Plaskolite Acrylic PL-30 | Plaskolite, Inc. | Acrylic (PMMA) | Plaskolite Acrylic |
| Hifax CB 1160 G1 C11538 | LyondellBasell Industries | PP Copolymer | Hifax |
| CYCOLOY™ C6200 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |