Daelim Po1y® XP9100S
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GmlNiH_DaelimPo1yXP9100S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP9100S is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®XP9100S application areas include bags/linings, wrappers, movies and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 57.9 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 53.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 630 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 250 | g | ASTM D1709A |
| Seal Initiation Temperature 1(50 µm, Blown Film) | 120 | °C | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1004 | ||
| Lateral flow : 0.0500mm | 152 | kN/m | ASTM D1004 |
| Traffic : 0.0500mm | 142 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Peak Melting Temperature | 122 | °C | ASTM D3418 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 85 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | HGT, 2.8 kg, 0.5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7795 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SMOKEGUARD™ O 301 NATURAL | AlphaGary | Polyolefin, Unspecified | SMOKEGUARD™ O |
| Huaxia Shenzhou FKM DS2603-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| LUBEMIX 65 BLACK | LUBEN PLAST srl | PC+ABS | LUBEMIX |
| Polygen ASG6C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |