OmniPro™ TPO 20M HC
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gmk5ZG_OmniPro-TPO-20M-HC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact Resistance, Easy Flow, Enhanced Clarity, Thermoplastic Polyolefin |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 19.3 | MPa | ASTM D638 |
| Flexural Modulus | 758 | MPa | ASTM D790 |
| Flexural Strength | 21.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 320 | J/m | |
| 23°C, 3.18 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 65.6 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 2700 | RTP Company | TPE | RTP |
| Taitarex® 866N / B | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| VITAMIDE® AY34NT6300 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Cheng Yu IPS600 | Cheng Yu Plastic Company Limited | PS (HIPS) | Cheng Yu |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (MECESA) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |