Borealis PP BC612WG
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GmGOPG_Borealis-PP-BC612WG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BC612WG is a polypropylene copolymer intended for injection moulding. The product is available in natural but other colours can be provided on request. This material has excellent balanced mechanical properties and is easy to process. Applications BC612WG has been developed especially for applications like: Washing machine parts Dishwashers components Household applications Special features: Long term high heat stabilised UL registered under File E108112 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 2.00mm | 1.4 | % | Internal method |
| Flow direction : 2.00mm | 1.6 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 44.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 87 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 51.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 64.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3899 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP ESD C 260H | RTP Company | Nylon 66 | RTP |
| VITAMIDE® AO3XBK6569 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| ELASTOSIL® M 4511 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| Laprene® 8ST193A80/T2 | SO.F.TER. SPA | SEBS | Laprene® |